When casting began, hand to suppress the automatic adjustment of plug, blocking the flow nozzle, mixing furnace cut eye, so that the inflow of molten aluminum through the chute dispensing tray until liquid aluminum reaches 2/5 in dispensing tray, automatic release adjusting plug, aluminum flow into the mold, the molten aluminum that is cooling in the chassis. When the liquid reaches 30mm high aluminum in the mold to drop the chassis, and began to send cooling water and automatically adjust stopper control the inflow of molten aluminum mold in a balanced manner, copper ash and molten aluminum to maintain a constant height within the mold . Scum on the surface of the liquid aluminum oxide film to be promptly removed. When the ingot length of about 6m, blocked stove eye, removed the dispensing tray until after all solidification of molten aluminum to stop water supply, the water jacket is removed, the cast ingot out with a monorail, in accordance with the requirements of size sawing amputated, and then prepare for the next casting. Aluminum liquid flow into the mold through the flow cell, with a shovel aluminum surface oxide film is removed, called slag. Flow over a mold, it will move to the next chute mold for the continuous casting machine is moving forward. Mold in turn forward, gradually cooling molten aluminum, copper ash prices reach central casting machine aluminum liquid has solidified into ingots, melting marked by the printer number. When the aluminum ingot casting machine reaches the top, has been completely solidified into ingots, then flip the mold, copper ash, aluminum ingot stripping out copper ash falls automatically pick ingot small car, automatic stacking the stacker , bundling becomes finished aluminum ingots. Casting machine from the water cooling, but you must start before the water after casting machine turn full circle. 8-10t consumption per ton of aluminum was about water, summer hair needs to be attached to the surface cooling. Belonging to a flat die casting ingot, the solidification of liquid aluminum is bottom-up direction, and the upper middle of the final solidification, leaving a gutter-collapsed. Ingots various parts of the coagulation time and conditions vary, so its chemical composition will be different, but the whole is standard. Copper ash | copper ash | Sun Shine scrap metal recycling (view) recovered from the Linyi City Shengxin scrap metal Limited. Linyi City Shengxin scrap metal recycling Ltd. (shengxin.tz1288.com) is a professional, "scrap metal, alloy, machine aluminum, brass, wine together, miscellaneous aluminum, copper ash, zinc ash, zinc slag" of the company. Since its inception, we adhere to the "good faith, sound management" approach, the courage to participate in healthy competition in the market, so that the "lead ingots, scrap metal, alloy, machine aluminum, brass, wine together, miscellaneous aluminum, copper ash, zinc ash, zinc "brand has a good reputation. We adhere to the "service first, customer first" principle, so Shengxin scrap metal recycling scrap metal won in the public trust of customers, and establish a good corporate image. Special Note: This information is for reference only pictures and information, please contact us to obtain the most accurate information, thank you!