A series of deformation of aluminum alloy: 1000 series aluminum alloy 1050, 1060 on behalf of the 1100 series. In all series, 1000 series is the largest aluminum content of series. It can reach more than 99.00% purity. Because it does not contain other technical elements, so the production process is relatively simple, relatively cheap price, engine recovery, is currently the most commonly used conventional industry a series. Most of the market circulation of 1050 and 1060 series. 1000 series aluminum according to the last two digits to determine the minimum aluminum content of the series, such as the 1050 series the last two digits of 50, named according to the principle of international brands, car engine recovered, aluminum content must reach more than 99.5% of qualified products. Our technical standard aluminum (gB / T3880-2006) is also clear that 1050 aluminum content of 99.5%. By the same token 1060 series aluminum, aluminum content must be 99.6%. Silicon carbide has a corrosive effect on. While the general will be more than 12% Si aluminum alloy called high silicon aluminum alloy, it is recommended to use diamond cutter, but this is not absolute, the silicon content gradually increased the destructive power of the tool is also gradually increasing. Therefore, some manufacturers in the silicon content of more than 8% on the recommended use of diamond tools. Aluminum silicon content of between 8% -12% of a transition zone, both can use ordinary carbide, diesel engines recovery, you can also use diamond tools. But the use of carbide should be used by PVD (Physical layer) method, no aluminum elements, the film thickness of smaller tools. Because PVD method and a small film thickness of the tool to maintain a more sharp cutting edge as possible (otherwise, avoid abnormal growth at the edge of the film needs to be sufficient edge passivation, recycling waste engine, cutting aluminum on will not sharp), and film material containing aluminum film may cause blade damage in conjunction with the workpiece material and tool substrate film and cooperate with the pro. Superhard coatings because more aluminum compounds, nitrogen, three of titanium, cemented carbide substrate may be due to a small amount of flaking caused by chipping over the film when peeled. Recycling scrap engine, Shengxin scrap metal recycling (online consultation), the engine from the Linyi City Shengxin Recycling scrap metal Limited. Linyi City Shengxin scrap metal recycling Ltd. (shengxin.tz1288.com) Shandong Linyi, leading scrap metal, over the years, the company is implementing the scientific management, innovation and development, the principle of honesty and trustworthiness, and satisfy customer needs. In Shengxin scrap metal recycling leadership with the staff warmly welcome all inquiries negotiations to create Shengxin scrap metal recycling better future.